Bishii Luulyo 13, 2023, kooxda Prof. Gang Wang ee Machadka Cilmi-baarista Qalabka ee Jaamacadda Shanghai ayaa daabacday natiijooyinkoodii ugu dambeeyay ee cilmi-baarista "Kobcinta qaab-dhismeedka qaab-dhismeedka iyo sifooyinka farsamada ee (FeCoNi) 85.84Al7.07Ti7.09-gacanta sare ee entropy iyadoo la dhalaalayo laser la xushay daawaynta gabowga", kaas oo adeegsada habka wax soo saarka wax-ku-darka aadka u hufan iyo habka gabowga muddada-gaaban si loo soo saaro ((FeCoNi)85.84Al7.07Ti7.09) daawaynta sare ee entropy.FeCoNi) 85.84Al7.07Ti7.09 High-entropy alloy, kaas oo soo bandhigaya sifooyin farsamo oo aad u fiican, oo leh awoodda ugu dambeysa ee 1625 MPa, awoodda wax-soo-saarka 1214 MPa, iyo dhererka jebinta 11.6%.Professor Jia Yandong iyo Dr. Mu Yongkun waa qorayaasha wada xidhiidhsan.
Natiijooyinka muhiimka ah
Shaqadani waxay baadhay saamaynta daawaynta gabowga ee kobaca qaabdhismeedka yar yar iyo sifooyinka farsamada (FeCoNi)85.84Al7.07Ti7.09HEA ay soo saartaySLM.Gabagabada soo socota ayaa la soo saaray.
(1) Laba hab oo xoojin ah, xoojinta kala-baxa iyo xoojinta roobabka, ayaa lagu soo bandhigay FCNAT HEA iyadoo la adeegsanayoSLMfarsamada iyo daawaynta gabowga wakhtiga gaaban ee 780°C.Natiijo ahaan, isku-darka kala-baxyada cufnaanta sare iyo wejiyada degdega ah ayaa lagu gaari karaa FCNAT 780, taasoo keentay sifooyinka farsamaysan ee ugu fiican (xoogga soo saarista σ0.2, xoogga ugu dambeeya ee σUTS, iyo elongation at qiimaha jebinta εf 1214 MPa, 1625 MPa iyo 11.6% siday u kala horreeyaan).
(2) Halabuurka wejiga eeSLMshaybaarada iyo muunadaha da'da ayaa inta badan ka kooban wajiga FCC, wejiyada L12 iyo L21.Daawaynta gabowga ka dib, wejiyada L12 iyo L21 ayaa soo degdegay iyo nuxurka wejiyada L12 iyo L21 ayaa si tartiib tartiib ah hoos ugu dhacay kororka heerkulka daaweynta gabowga.
Haddii aad rabto inaad ogaato macluumaad dheeraad ah oo aad u baahan tahay inaad samayso qaabka daabacaadda 3d, fadlan la xidhiidhJSADD 3D soo saarahamar kasta.
Qore: Yolanda/Lili Lu/Seazon