I-SLA Resin Rubber njenge-White ABS njenge-KS198S

I-SLA Resin Rubber njenge-White ABS efana ne-KS198S Isithombe Esifakiwe

Incazelo emfushane:

Uhlolojikelele Lwempahla
I-KS198S iyinhlaka ye-SLA emhlophe, eguquguqukayo enezici zokuqina okuphezulu, ukunwebeka okuphezulu nokuthinta okuthambile.Ilungele ukuphrinta isibonelo sezicathulo, ukugoqa kwerabha, imodeli ye-biomedical nezinye izingxenye zenjoloba njengezingxenye.

Thumela i-imeyili kithi Ukulanda Ishidi Ledatha

Imininingwane Yomkhiqizo

Omaka bomkhiqizo

Inzuzo

- Ukuguquguquka okuphezulu

- Ukumelana kahle nezinyembezi

- Inembile kakhulu

- Umbala omhlophe omuhle kakhulu

Izicelo Ezikahle

- Izicathulo

- Ama-prototypes adinga irabha njengempahla

- Amamodeli wokubonisa amhlophe athambile

I-Liquid Properties

Ukubukeka	Emhlophe	Dp	13.5 mJ/cm2	[ukuchayeka okubalulekile]
I-Viscosity	560 cps@30℃	Ec	0.125 mm	[slope of cure-depth vs. In (E) curve]
Ukuminyana	1.1 g/cm3	Ugqinsi lwesendlalelo sokwakha	0.08-0.12 mm

Izakhiwo Zemishini		I-UV Postcure
ISILINGANISO	INDLELA YOKUHLOLA	VALUE
Ukuqina, Shore D	I-ASTM D 2240	72-78
Flexural modulus , Mpa	I-ASTM D790	2,680-2,775
Amandla e-Flexural , Mpa	I-ASTM D790	65-75
I-tensile modulus, i-MPa	I-ASTM D638	2,170-2,385
Amandla aqinile, i-MPa	I-ASTM D638	25-30
Ukwandisa ngesikhathi sekhefu	I-ASTM D638	12 -20%
Amandla omthelela, i-notched lzod, J/m	I-ASTM D 256	58-70
Izinga lokushisa lokuphambuka kokushisa, ℃	I-ASTM D 648 @66PSI	50-60
Ukuguqulwa kwengilazi, Tg	I-DMA, E”peak	55-70
Ukuminyana , g/cm3		1.14-1.16

Izinga lokushisa elinconyiwe lokucubungula nokugcinwa kwe-resin engenhla kufanele libe ngu-18℃-25℃.
1e aoned te tcreo orertlroleoep ndecerece.rhe syes d wbah ma ey dpnton nbirdualrmathrero.srg reorot-rg rcices.I-shet es gie in aboe sfor niometon purpsis ry andovs rot cortitutealeal bnig MS.

Okwedlule: Okuhle Kakhulu Okungafihli kwe-SLA Resin PMMA njenge-KS158T2e

Olandelayo: Amandla Aphezulu Nokuqina Okuqinile kwe-ABS njenge-SLA Resin Light Yellow KS608A