Discount wholesale Direct Metal Laser Melting - Ideal for Strong Functional Complex Parts MJF Black HP PA12 – JS ADDITIVE

Product Detail

, , ,

Discount wholesale Direct Metal Laser Melting - Ideal for Strong Functional Complex Parts MJF Black HP PA12 – JS ADDITIVE Detail:

Excellent chemical resistance

Good functionality and mechanical properties

Good waterproof performance

Category	Measurement	Value	Method
General properties	Powder melting point (DSC)	187 °C/369 °F	ASTM D3418
	Particle size	60 µm	ASTM D3451
	Bulk density of powder	0.425 g/cm3	ASTM D1895
	Density of parts	1.01 g/cm3	ASTM D792
Mechanical properties	Tensile strength, max load9 , XYTensile strength, max load9 , ZTensile modulus9 , XYTensile modulus9 , ZElongation at break9 , XY Elongation at break9 , Z Flexural strength (@ 5%)10 , XY Flexural strength (@ 5%)10 , Z Flexural modulus10 , XY Flexural modulus10 , Z Izod impact notched (@ 3.2 mm, 23ºC), XYZ	48 MPa/6960 psi	ASTM D638
Thermal properties	Heat deflection temperature (@ 0.45 MPa, 66 psi), XYHeat deflection temperature (@ 0.45 MPa, 66 psi), ZHeat deflection temperature (@ 1.82 MPa, 264 psi), XYHeat deflection temperature (@ 1.82 MPa, 264 psi),Z	48 MPa/6960 psi	ASTM D638
		1700 MPa/247 ksi	ASTM D638
		1800 MPa/261 ksi	ASTM D638
		20%	ASTM D638
		15%	ASTM D638
		65 MPa/9425 psi	ASTM D790
		70 MPa/10150 psi	ASTM D790
		1730 MPa/251 ksi	ASTM D790
		1730 MPa/251 ksi	ASTM D790
		3.5 kJ/m2	ASTM D256 Test Method A
		175 ºC/347 ºF	ASTM D648 Test Method A
		175 ºC/347 ºF	ASTM D648 Test Method A
		95 ºC/203 ºF	ASTM D648 Test Method A
		106 ºC/223 ºF	ASTM D648 Test Method A
Recyclability	Refresh ratio for stable performance	20%
Certifications	USP Class I-VI and US FDA guidance for Intact Skin Surface Devices, RoHS11, EU REACH, PAHs