Pepa ʻikepili ʻenehana
| Waiwai Waiwai | ʻAno Optical | ||
| Ka nana aku | Akaka | Dp | 0.135-0.155 mm |
| ʻO ka viscosity | 325 -425cps @ 28 ℃ | Ec | 9-12 mJ/cm2 |
| ʻO ka mānoanoa | 1.11-1.14g/cm3 @ 25 ℃ | Mānoanoa papa hale | 0.1-0.15mm |
| Na Waiwai Mechanical | UV Postcure | |
| ANA | HANA HO'O | WAIWAI |
| Paʻakiki, Kahakai D | ASTM D 2240 | 72-78 |
| Hoʻololi hoʻololi, Mpa | ASTM D 790 | 2,680-2,775 |
| Ka ikaika wiliwili , Mpa | ASTM D 790 | 65- 75 |
| ʻO ka modulus tensile , MPa | ASTM D 638 | 2,170-2,385 |
| Ka ikaika tensile , MPa | ASTM D 638 | 25-30 |
| Elongation i ka wā hoʻomaha | ASTM D 638 | 12 -20% |
| Ka ikaika o ka hopena, ka lzod notched, J/m | ASTM D 256 | 58 - 70 |
| ʻO ka wela wela, ℃ | ASTM D 648 @66PSI | 50-60 |
| Hoʻololi aniani, Tg | DMA，E” peak | 55-70 |
| ʻO ka mānoanoa , g/cm3 | 1.14-1.16 | |
ʻO ka mahana i manaʻo ʻia no ka hana ʻana a me ka mālama ʻana i ka resin ma luna nei he 18 ℃-25 ℃
Hoʻokumu ʻia ka ʻikepili i luna ma luna o kā mākou ʻike a me kā mākou ʻike i kēia manawa, ʻokoʻa paha nā kumukūʻai a hilinaʻi ʻia i ka hoʻoili ʻana o ka mīkini a me nā hana post-curing.ʻO ka ʻikepili palekana i hāʻawi ʻia ma luna nei no ka ʻike ʻike wale nō a
ʻaʻole ia he MSDS paʻa i ke kānāwai.
-
ʻO ka pale wela kiʻekiʻe SLA Resin ABS like ...
-
ʻOi aku ke kiʻekiʻe o ka wela wela SLA Resin Bl...
-
Ka ikaika kiʻekiʻe a me ka ikaika ikaika ABS like ...
-
Ka ikaika kiʻekiʻe a me ka paʻakikī SLS Nylon...
-
ʻO SLA Resin Rubber e like me ke Keʻokeʻo ABS e like me KS198S
-
ʻO ke kino o ka ʻili maikaʻi a me ka paʻakikī maikaʻi SLA A...