Lembar Data Téknis
- Transparansi anu saé
- Kalembaban anu saé sareng résistansi Uap
- Gancang ngawangun sarta gampang fifinish
- Akurat jeung diménsi stabil
Aplikasi idéal
- Lénsa otomotif
- Botol sareng tabung
- Prototipe fungsional tangguh
- Modél tampilan transparan
- Analisis aliran cairan
Téknis Data-lambar
| Pasipatan cair | Pasipatan optik | ||
| Penampilan | Jelas | Dp | 0,135-0,155 mm |
| Viskositas | 325 -425cps @ 28 ℃ | Ec | 9-12 mJ/cm2 |
| Kapadetan | 1.11-1.14g/cm3 @ 25 ℃ | Ketebalan lapisan wangunan | 0,1-0,15 mm |
| Sipat mékanis | UV Postcure | |
| PANGUKURAN | METODE UJI | NILAI |
| Teuas, Shore D | ASTM D 2240 | 72-78 |
| Modulus lentur, Mpa | ASTM D 790 | 2.680-2.775 |
| Kakuatan lentur, Mpa | ASTM D 790 | 65-75 |
| modulus tegangan, MPa | ASTM D 638 | 2.170-2.385 |
| Kakuatan tensile, MPa | ASTM D 638 | 25-30 |
| Elongation dina putus | ASTM D 638 | 12 -20% |
| Kakuatan dampak, notched lzod, J/m | ASTM D 256 | 58 - 70 |
| Suhu defleksi panas, ℃ | ASTM D 648 @66PSI | 50-60 |
| Transisi kaca, Tg | DMA, E"puncak | 55-70 |
| Kapadetan, g/cm3 | 1.14-1.16 | |
Suhu anu disarankeun pikeun ngolah sareng neundeun résin di luhur kedah 18 ℃ -25 ℃
Data di luhur dumasar kana pangaweruh jeung pangalaman urang ayeuna, nilai nu bisa rupa-rupa sarta gumantung kana processing mesin individu jeung prakték pos-curing.Data kaamanan anu dijelaskeun di luhur ngan ukur kanggo tujuan inpormasi sareng
henteu janten MSDS anu mengikat sacara sah.